Bradite HB MIO Build Finish Coat AM60 is a high build modified alkyd based micaceous iron oxide coating and finish which gives excellent anti-corrosive properties when used as a coating or finish in a conventional paint system.
Bradite HB MIO Build Finish Coat AM60 is perfect for the protection and decoration of ferrous & non-ferrous metals either as an intermediate build coat or finish. For all suitably primed ferrous & non-ferrous metals which are dry, free of contamination, dust and have been properly prepared and/or primed. Compatibility with existing coatings should be confirmed by preparing and painting a test area.
Application and use should always conform to the codes of practice described in BS 6150 and BS 5493. Best results are obtained by spraying.
High pressure steam cleaning to remove all loose, flaking paint and contamination back to a sound surface. Bradite TD39 industrial strength detergent, washing and rinsing should be used with scrubbing to remove grease or oil.
Remove all rust scale, loose mill scale or other corrosion products by scraping and mechanical cleaning to SIS-St 3 (ISO 8501-1:1998). Intact areas of existing coatings should be roughened by abrasive manual or disc sanding, feathering back to a sound coating edge. Cracks and pits should be filled using a suitable metal filler before painting. Substrate should be dust free and completely dry before coating.
Light surface rusting may be effectively treated using one coat of Bradite Rust Converter RC46 prior to application of this product. New galvanised steel should be thoroughly degreased and then pre-treated with Bradite Mordent Solution TM38 prior to application of this product. Alternatively, or for other non-ferrous metals, prime with Bradite Barrier Primer EU96 before application of this product.
For the protection of metal structures subject to more demanding exposure scenarios, application of Fastrac Antico Primer AP71 , prior to finishing with this product, is highly recommended.
Certificates & Approvals
- Manufactured under the auspices of an ISO 9001:2008 quality & ISO 14001:2004 environmental management systems.
- Conforms to MOD TS10201 specification & BS5493 parts FU2C/FF3D.
- British gas reference BGC BU2, BU3, BU4.
|Stock Colours:||Silver Grey and Colours listed above only|
|VOC Content:||411 g/L|
|Suitable Substrates:||Suitably prepared steel degreased, blast clean to SIS-Sa 21/2 min or mechanical/manually prepared to SIS-Sa 3 min. Previous suitable coat dry, clean and abraded as necessary.|
|Application Method:||Brush, Roller, Airless Spray or conventional Air Spray|
|Theoretical Coverage:||12 m2/L/coat|
|Wet Film Thickness (WFT):||100 microns/coat|
|Dry Film Thickness (DFT):||48 microns/coat|
|Surface Dry:||4 hours at 20°C|
|Overcoatable:||After minimum of 16 hours at 20°C|
|Fully Cured:||7 days at 20°C|
|Cleaner / Thinner:||Bradite Thinner TW35|
|Shelf Life:||12 months minimum in original unopened containers|
|Packaging:||Available in 4.5 Litres|
The manufacturers data sheets are available for download from this website. It is your responsibility to read and understand all aspects of the data sheets before you place an order and prior to application. Please pay special attention to the preparation, mixing and application temperatures of the product, cleaning of substrate and environmental factors such as temperature, rain etc. Quoted coverage rates are based on the manufacturers theoretical rates and may vary depending upon substrates absorption, texture and application. We always recommend a test is carried out to ensure suitability.