Remmers Epoxy MT 100

SKU
id17639
Part A: UN3082 (Class: 9, Pk Grp: III), Part B: UN2735 (Class 8, Pk Grp: II)
Special primer for matt damp substrates based on a transparent epoxy resin.
Available in 10 Kg and 25 Kg
From £287.24 £239.37
In stock
Only %1 left
Product Description

Remmers Epoxy MT 100 is a special primer for matt damp substrates based on a transparent epoxy resin. It can be subjected to both mechanical and chemical loads and is free from plasticisers and nonylphenols.

Best Uses

Remmers Epoxy MT 100 is an unpigmented epoxy resin binder that is best used as an impregnation agent, primer, bonding layer, levelling layer and for the production of compression resistant mortars, flow mortars as well as a blinded layer for blinded covers.

Application

The substrate must be firm, dimensionally stable, capable of bearing loads and free of loose constituents, dust, oil, grease, rubber marks and other substances that could interfere with adhesion. The tensile strength of the surface of the substrate must be at least 1.5 N/mm² on average (smallest individual value of at least 1.0 N/mm²), and the compressive strength must be at least 25 N/mm². The substrate can be slightly moist but without liquid film on the surface and should not be exposed to major temperature swings (vapour pressure). In this case the primer must always be applied twice.

  • Concrete max 6 m% humidity
  • Cement Screed max. 6 m% humidity

The substrate must be protected from exposure to moisture from underneath during utilisation. Weak absorbing substrates must be tested with regard to their suitability for coating, if necessary a trial surface must be set up. If the product is used on green concrete (water–cement ratio < 0,45) the substrate must be suitable for blasting or grinding.

Prepare the substrate by suitable means, e.g. steel ball jetting or diamond grinding, so that it meets the requirements specified above. Broken out or missing areas in the substrate should be filled flush with the surface using Remmers PCC systems or Remmers EP mortars.

Conditions for use

Temperature of material, surroundings and substrate: min. +5 °C - max. +25 °C. During the curing process, the applied material should be protected from moisture which could impair the surface and impair the adhesion. Relative humidity should not exceed 80%. The temperature of the substrate must be at least 3 °C above the dew point temperature during application and curing.

Technical Details

Systems

  • Remmers SS330 - Epoxy Flex PH Systems (DFT = 350 - 400µ)
  • Remmers SS 343TFL - QP Color Pro System (DFT = 1-2mm)
  • Remmers SS350PH+ - Epoxy Self Smoothing System with Performance Seal (DFT = 2-3mm)
  • Remmers 356WHG - Epoxy Conductive with Excellent Chemical Resistance System (1.5 - 2mm)
  • Remmers SS 356 - ESD Epoxy Self Smoothing Screed System (DFT = 2-3mm)
  • Remmers 356WHG - Epoxy Conductive with Excellent Chemical Resistance System (1.5 - 2mm)

See technical tab for downloadable System Sheets.

Notes

Unless otherwise specified, all of the values and application rates given above have been determined under laboratory conditions (20 °C). Slight deviations from these values may arise if the product is worked with on site. Primers must always be applied so that all pores are filled; it may therefore be necessary to increase the application rate or to apply a second coat. As mineral substrates have different absorption capacities, impregnated surfaces have a spotted appearance. Not suitable for high-visibility surfaces.

When coating continuous surfaces, only use materials with the same batch number as slight differences in colour, gloss and texture may occur. Abrasive mechanical loads leave traces of wear. Epoxy resins are generally not colourfast when exposed to UV light or weather. Further notes on working, system construction and maintenance of the listed products can be found in the latest Technical Data Sheets and the Remmers system recommendations.

Technical Info

Components: 2 Component Set
Type: Primer
Finish: -
Stock Colours: -
Tintable: No
VOC Content: < 500 g/l
Volume Solids: -
Suitable Substrates: Concrete, Cement Screeds
Application Method: Smoothing trowel, Toothed Trowel, Epoxy Roller, Spiked Roller
Theoretical Coverage: Approx. 0.30 - 0.50 kg/m² of binder (depending on the substrate)
Wet Film Thickness (WFT): -
Dry Film Thickness (DFT): -
Mixing Time: 3 Minutes
Pot Life: 25 Minutes
Waiting Time: Min 6 hours and max 24 hours
Drying Time: Foot Traffic after 8 hours, Mechanical Loads after 2 days
Fully Cured: Full loading capacity after 5 days
Cleaner / Thinner: Thinner V 101 
Shelf Life: 2 years unopened
Packaging: Available in 10 Kg and 25 Kg tins