Bradite Epoxy Barrier Primer is best used as a barrier primer for suitably prepared steel and non-ferrous substrates. It provides outstanding adhesion and excellent corrosion protection. It may also be used as a wet blast primer and for immersion application when part of a suitable coating system.
For internal & external steel & non-ferrous substrates which are dry, free of contamination and have been properly prepared.
Application and use should always conform to the codes of practice described in BS 6150 and BS 5493.
Brush and Roller – supplied ready for use. Thin, if required, with 0 - 5% Bradite Thinner TE36.
Conventional Air Spraying - Thin with 10 - 25% Bradite Thinner TE36 as required, tip size – 23 thou (1.7mm), tip pressure 60psi (0.4MPa) approximately.
Airless Spraying - Thin with 0 - 25% Bradite Thinner TE36 as required, tip size - 18 thou (0.46mm) approximately, tip pressure - 2100 psi (15MPa) approximately.
Components: | Two Pack |
Type: | Solvent Based |
Finish: | Eggshell (approx. 20%) |
Stock Colours: | Yellow |
Tintable: | No |
VOC Content: | 429 g/L |
Volume Solids: | 50% (mixed) |
Suitable Substrates: | Steel and non-ferrous substrates |
Application Method: | Brush, Roller, Airless Spray or Air-Atomised Spray |
Theoretical Coverage: | 10 m2/L/coat |
Wet Film Thickness (WFT): | 100 microns/coat |
Dry Film Thickness (DFT): | 50 microns/coat |
Induction Time: | - |
Pot Life: | 14 hours at 20°C |
Touch Dry: | 30 minutes at 20°C |
Overcoatable: | After 8 hours minimum to maximum of 3 months at 20°C |
Fully Cured: | - |
Cleaner / Thinner: | Bradite Thinner TE36 |
Shelf Life: | 12 months minimum in original unopened containers |
Packaging: | Available in 5 Litres |