Hempel Hempathane HS 55613

SKU
ID21303
Part A and B: UN1263 (Class: 3, Pk Grp: III)
A two-component semi-gloss acrylic polyurethane topcoat, cured with aliphatic isocyanate, with good gloss and colour retention.
Available in 5 and 20 Litres. Tintable to many RAL and BS shades.
From £79.61 £66.34
In stock
Only %1 left
Product Description

Hempel Hempathane HS 55613 is a two-component semi-gloss acrylic polyurethane topcoat, cured with aliphatic isocyanate, with good gloss and colour retention. Contains zinc phosphate.

Best Uses

Hempel Hempathane HS 55613 is formulated as a VOC-compliant, high-build finishing coat for protection of structural steel in a corrosive environment. May be specified as a one coat "Direct To Metal" system in environments classified as C2 and C3.

Application

Prepare according to specification. Apply only on a dry and clean surface with a temperature above the dew point to avoid condensation. Minimum temperature for curing is: -10°C/14°F At the freezing point and below be aware of the risk of ice on the surface, which will hinder adhesion. The film formation may be adversely affected by light rain, high humidity and/or condensation during application and the following interval after application: 8 hours, 20°C/68°F In confined spaces provide adequate ventilation during application and drying.

When specified as a one coat "Direct to Metal"-system, follow "Good Painting Practice" and apply stripe coating before the spray application on areas difficult to cover properly by spray application. Even small traces of water in the mixed paint will reduce the pot life and result in film defects.

IMPORTANT NOTICE: From 24th August 2023, adequate training is required before industrial or professional use of this product. Training can be accessed at: https://www.safeusediisocyanates.eu

Technical Details
Components: Two Pack
Type: Acrylic Polyurethane
Finish: Semi Gloss
Stock Colours: 11150 Grey
Tintable: Yes, call our Sales Team to check certain shades. Please note, bespoke tints are non refundable / exchangeable
VOC Content: 384 g/L
Volume Solids: 57%
Suitable Substrates: For protection of structual steel
Application Method: Airless Spray or Brush
Theoretical Coverage: 5.7 m2 per litre per 100 microns
Wet Film Thickness (WFT): 175 microns
Dry Film Thickness (DFT): 100 microns
Induction Time: -
Pot Life: 2 hours at 20°C
Surface Dry: 45 minutes at 20°C
Overcoatable: Dependant on Specification
Fully Cured: 7 days at 20°C
Cleaner / Thinner: Hempel Thinner 08080
Shelf Life: 3 years for BASE and 2 years (25°C/77°F) for CURING AGENT from time of production
Packaging: Available in 5 and 20 Litres