International Interzone 1000

SKU
id18960
Part A: UN1263 (Class: 3, Pk Grp: III), Part B: UN3066 (Class: 8, Pk Grp: II)
A very high solids, low VOC, two component high build epoxy containing a high level of chemically resistant glass flake.
Available in 18 Litres
From £557.99 £464.99
In stock
Only %1 left
Product Description

International Interzone 1000 is a very high solids, low VOC, two component high build epoxy containing a high level of chemically resistant glass flake which imparts properties of excellent corrosion, abrasion and chemical resistance.

Best Uses

International Interzone 1000 is formulated for the protection of steelwork in areas where high abrasion and corrosion resistance are required including splashzone areas on offshore platforms, jetties, decks, bridges, chemical plants, pulp and paper mills, and water treatment plants. Excellent resistance to cathodic disbondment, gives good compatibility with both sacrificial anode and impressed current systems, making Interzone 1000 particularly suitable for the long term protection of sub-sea structures. As part of a non-slip deck system in conjunction with appropriate aggregate.

Application

All surfaces to be coated should be clean, dry and free from contamination. Prior to paint application all surfaces should be assessed and treated in accordance with ISO 8504:2000. Oil or grease should be removed in accordance with SSPC-SP1 solvent cleaning.

Abrasive Blast Cleaning
Abrasive blast clean to Sa2½ (ISO 8501-1:2007) or SSPC-SP10. If oxidation has occurred between blasting and application of Interzone 1000, the surface should be reblasted to the specified visual standard. Surface defects revealed by the blast cleaning process should be ground, filled, or treated in the appropriate manner.
A sharp, angular surface profile of 75-100 microns (3-4 mils) is recommended.

Primed Steelwork
Interzone 1000 can be applied over approved anti-corrosive primers. The primer surface should be dry and free from all contamination and Interzone 1000 must be applied within the overcoating intervals specified (consult the relevant product data sheet). Areas of breakdown, damage etc., should be prepared to the specified standard (e.g. Sa2½ (ISO 8501-1:2007) or SSPC-SP10 Abrasive Blasting, or SSPC-SP11, Power Tool Cleaning) and patch primed prior to the application of Interzone 1000 Weld seams and damaged areas should be blast cleaned to Sa2½ (ISO 8501-1:2007) or SSPC-SP10. If the shop primer shows extensive or widely scattered breakdown overall sweep blasting may be necessary.

Technical Details

Approvals

  • Norsok M-501 System 1 (Pre Qualified)
  • Norsok M-501 System 7A (Pre Qualified)
  • Norsok M-501 System 7B (Pre Qualified)
  • Norsok M-501 System 7C (Pre Qualified)

Compatibility

Interzone 1000 will normally be applied directly to correctly prepared steel, however, the following primers are recommended:

The following topcoats are recommended for Interzone 1000:

Technical Info

Components: Two Part
Type: Glass Flake
Finish: -
Stock Colours: Limited Colour Range
Tintable: No
VOC Content: 70.0g per Litre
Volume Solids: 92%
Suitable Substrates: For steelwork
Application Method: Brush, Air Atomised Spray or Airless Spray
Theoretical Coverage: 1.8m2 per litre at 500 microns
Wet Film Thickness (WFT): 543 - 1087 microns
Dry Film Thickness (DFT): 500 - 1000 microns
Induction Time: -
Pot Life: 3 hours at 15°C
Touch Dry: 8 hours at 15°C
Overcoatable: 18 hours to 5 days at 15°C
Hard Dry: 18 hours at 15°C
Cleaner / Thinner: International GTA822 or International GTA415
Shelf Life: 18 months minimum at 25°C
Packaging: Available in 18 Litres