PPG Steelguard 564 is a one component, thin-film, solvent borne, intumescent coating designed for providing fire protection to structural steelwork in an industrial environment.
PPG Steelguard 564 has been tested to national and international standards and can be used in dry, internal environments without the use of a protective topcoat. Steelguard 564 is an excellent fire resistant product that provides up to 120 minutes of protection from cellulosic fires and provides surface with 12 months of weather resistance, when no topcoat is used, providing the structure is not immersed in water or exposed to high humidity.
PPG Steelguard 564 intumescent coating can be applied using airless spray for optimum performance and a brush should only be used for touch ups and small tricky areas. Steelguard 564 should not be applied below 5°C or above 50°C, otherwise it may not adhere to the surface properly. With quick drying time 564 is dry in just 20 minutes and can be recoated after 4 hours in conditions of around 20°C.
IMPORTANT INTUMESCENT PRODUCT NOTE: Always contact Promain’s technical team prior to purchase to obtain a tailored project specification and the advice necessary. The information displayed on this website should only be used as a guide. Promain UK Limited will not be held liable for any resulting damage to property, human life or monetary costs incurred due to incorrect specification, preparation, application or maintenance that has occurred due to negligence by either the purchaser or applicator. This includes your failure to have contacted us to obtain the relevant advice/specification.
Surface and Environment
PPG Steelguard 564 can be used of on-site or off-site application and when dry produces a high quality, white/grey matt, protective coating that can be used internally or externally to ensure that structural steel has the utmost protection from the risk of fire.
- Intumescent coating
- Offers up to 120 minutes of protection from cellulosic fires
- Provides surface with 12 months of weather resistance
- can be used of on-site or off-site application
|VOC Content:||327.0 g/l|
|Volume Solids:||75 +/- 3%|
|Suitable Substrates:||Structural Steelwork|
|Application Method:||Airless Spray. Brush or Roller should only be used on small areas (touch up and repair)|
|Theoretical Coverage:||1.07 m2/l for 700 microns|
|Wet Film Thickness (WFT):||-|
|Dry Film Thickness (DFT):||200 - 1000 microns (8.0 - 40.0 mils) per coat|
|Touch Dry:||20 minutes at 20°C|
|Overcoatable:||After minimum of 4 hours at 20°C|
|Cleaner / Thinner:||Thinner 21-06 (normally no thinner required. Use also as a cleaning solvent.|
|Shelf Life:||years from date of production unopened|
|Packaging:||Available in 20 and 200 Litres|
The manufacturers data sheets are available for download from this website. It is your responsibility to read and understand all aspects of the data sheets before you place an order and prior to application. Please pay special attention to the preparation, mixing and application temperatures of the product, cleaning of substrate and environmental factors such as temperature, rain etc. Quoted coverage rates are based on the manufacturers theoretical rates and may vary depending upon substrates absorption, texture and application. We always recommend a test is carried out to ensure suitability.