Sherwin Williams Magnalux 41V2
Please note, this product has a 20 day lead time on delivery.
Sherwin Williams Magnalux 41V2 is a glass flake vinyl ester acrylic co-polymer that is approved to NORSOK Rev 6 System 7A and 7B.
Best Uses
Sherwin Williams Magnalux 41V2 is formulated for immersion environments where superior resistance to chemical attack is required. This product is suitable for many chemical environments within the full pH range. Sherwin Williams Magnalux 41V2 has excellent resistance to de-mineralised water and good resistance to many solvents. It is also used in aggressive atmospheric or spillage conditions (bund areas).
Primer: For temperatures up to 85°C use Magnalux 42PP, for temperatures above 85°C use Magnalux 41VP. Sherwin Williams Magnalux 41V2 is overcoatable with itself or Magnalux 43VC.
Application
Blast clean to Sa2½ ISO 8501-1:2007. Surface profile in the range 75-125 microns. Ensure surfaces to be coated are clean, dry and free from all surface contamination.
Apply using airless spray. Use a brush for small areas or touch ups only.
Approvals
- Norsok M-501 System 7A (Pre Qualified)
Technical Info
| Components: | Three Pack |
| Type: | Glass Flake Vinyl Ester Acrylic Co-Polymer |
| Stock Colours: | Light Grey, Off White |
| Tintable: | No |
| Suitable Substrates: | For steel |
| Cleaner / Thinner: | Clean up with Sherwin Williams No.13. Do not thin |
| Shelf Life: | Base and catalyst (Hardener) 6 months, stored at temperatures below 20°C, away from heat sources and out of direct sunlight. Frequent temperature cycling will shorten storage life. |
| Packaging: | Available in 20 Litres |
| VOC Content: | <50 g/L |
| Application Method: | Airless Spray |
| Theoretical Coverage: | 1.8 m2 per litre at 500 microns |
| Finish: | Semi Gloss |
| Touch Dry: | 6 hours at 20°C |
| Fully Cured: | 3 - 4 days at 20°C |
| Volume Solids: | 41% |
| Pot Life: | 50 minutes at 20°C |
| Wet Film Thickness (WFT): | 555 microns |
| Dry Film Thickness (DFT): | 500 microns |