Sherwin Williams Resuflor HB CC

Sherwin Williams Resuflor HB CC is a two-pack, faster curing high performance floor coating based on high solids epoxy resin technology designed to provide a tough and durable floor protection finish in a variety of thicknesses and colours for a wide range of applications. Cures down to low temperatures.

Best Uses

Sherwin Williams Resuflor HB CC will provide a smooth gloss finish to which anti-slip aggregate can be added if required. Resuflor HB CC is easy to apply by roller and paint brush to create a seamless, hard wearing and hygienic floor finish. Suitable for application at lower temperatures as a cold cure material to ensure overnight curing where required.

• High build finish
• High solids
• Fast cure at ambient temperatures
• Excellent high gloss finish
• Low odour
• Hygienic and easily cleaned
• Good colour stability
• Excellent slip resistance with the inclusion of aggregates

Recommended for factory units, chemical plant rooms, engineering workshops, automotive and aviation areas. Also suitable coating for floors in food processing and beverage areas and warehouses as demarcation and walkways.

Application

New Concrete Floors: New concrete must be clean, sound, dry, fully cured and surface laitance removed by vacuum enclosed shot blasting or mechanical grinding, a minimum strength of 25 N/mm² is required.

Existing Concrete Floors: Remove all dirt, oil, grease, old paint or any other surface contaminants by vacuum enclosed shot blasting, scarifying or mechanical grinding. Fats, oils or greases must be removed by mechanical means and detergent washing and making sure all residue of detergent is washed and removed by rinsing with clean water. Local repairs should be carried out using Resuflor Patch.

Existing Floors (previously coated): All previous coatings and loose floor paints must be removed by mechanical preparation as described in the above section and primed as specified. If the old resin flooring cannot be removed then please consult with our technical team for advice on intercoat adhesion and suitability, as it may not be compatible with the existing floor coating.

Where Resucoat HB CC is applied to masonry/concrete surfaces, care must be taken to ensure that surface preparation is thorough but does not disfigure the surface.

Open and porous substrates should be primed with Resuprime ST on dry substrates only with less than 75% ERH reading. Where the Relative Humidity of a substrate exceeds 75% ERH Resuprime MVT should be specified and selected on the basis of hygrometer readings in accordance with BS 8203.

Where the Relative Humidity of a substrate exceeds 85% ERH Resuprime MVT should be specified and selected on the basis of hygrometer readings in accordance with BS 8203:2017. The number of coats to be applied is chosen in accordance with the following table:

• ERH% 75-85 - 1 coat of Resuprime MVT at 200 μm per coat
• ERH% 85-92 - 2 coats of Resuprime MVT at 200 μm per coat
• ERH% 92-97 - 3 coats of Resuprime MVT at 200 μm per coat

For further information please refer to recommended individual product data sheets.

Mix the entire contents of the base with the hardener. If a separate mixing bucket is being used mix thoroughly ensuring all contents of both components are removed from the buckets supplied. Mix using a slow speed electric mixer for approximately two to three minutes until the two components are fully combined.

The mixed unit should be applied immediately by roller, brush or squeegee with a consistent procedure. Floor areas should be cross-rolled to ensure even application and to minimise roller marks.