Jotun Jotacote Universal N10
Jotun Jotacote Universal N10 is a two component polyamine cured pure epoxy coating, benefiting from high solids, high build, abrasion resistance. Cures down to -10°C.
Best Uses
Jotun Jotacote Universal N10 is available with curing agents for standard, and for quick drying (QD) properties. Jotun Jotacote Universal N10 is specially designed as a universal, all round, all year, new building coating where fast dry to handle is required. Can be used as primer,
mid-coat, finish coat or as single coat system in atmospheric and immersed environments. Suitable for properly prepared aluminium, carbon steel, galvanised steel, shop primed steel and stainless steel substrate. It can be applied at sub-zero surface temperatures.
In marine environments, Jotun Jotacote Universal N10 is ideal for exterior and interior areas, including outside hulls, superstructures, decks, cargo holds and water ballast tanks. This product has very high flexibility, making it specially suitable for the temperature variation experienced in
crude oil, chemical and shuttle tankers. Approved for PSPC cross over testing with a wide range of shop primers.
- Cures down to -10°C
- Highly abrasion-resistant universal primer
- Universal application
- Most areas of new construction
- Low temperature application possible
- IMO PSPC for WBT and COT approved
Application
Preparation
- Carbon steel: Sa 2½ (ISO 8501-1)
- Stainless steel: Abrasive blast cleaning to achieve a surface profile using non-metallic abrasive media which is suitable to achieve a sharp and angular surface profile
- Aluminium: Abrasive blast cleaning to achieve a surface profile using non-metallic abrasive media which is suitable to achieve a sharp and angular surface profile
- Galvanised steel: Sweep blast-cleaning using non-metallic abrasive leaving a clean, rough and even pattern
- Shop primed steel: Sweep blasted or alternatively blasted to Sa 2 (ISO 8501-1) of at least 70 % of the surface
- Coated surfaces: Sa 2½ (ISO 8501-1)
Application
The product can be applied by:
- Spray: Use airless spray
- Brush: Recommended for stripe coating and small areas. Care must be taken to achieve the specified dry film thickness For QD version, brush is not recommended for temperatures above 15 °C
Roller: May be used for small areas. Not recommended for first primer coat. Care must be taken to achieve the specified dry film thickness. For QD version, roller is not recommended for temperatures above 15 °C
Approvals and Certifications
- Certified in accordance with IMO Res.215(82) – PSPC Water Ballast Tanks
- Certified in accordance with IMO Res.288(87) – PSPC Crude Oil Tanks
When used as part of an approved scheme, this material has the following certification:
- Low Flame Spread in accordance with EU Directive for Marine Equipment. Approved in accordance with parts 5
and 2 of Annex 1 of IMO 2010 FTP Code, or Parts 5 and 2 of Annex 1 of IMO FTPC when in compliance with IMO
2010 FTP Code Ch. 8
Technical Info
| Components: | Two Part |
| Type: | Polyamine cured pure epoxy |
| Finish: | Matt |
| Stock Colours: | Aluminium, aluminium red tone, black, buff, grey, red |
| Tintable: | No |
| VOC Content: | 261.0g per Litre |
| Volume Solids: | 72% |
| Suitable Substrates: | Aluminium, carbon steel, galvanised steel, shop primed steel and stainless steel substrate |
| Application Method: | Brush, Roller or Airless Spray |
| Theoretical Coverage: | 2.4 - 9.6 m2 per litre |
| Wet Film Thickness (WFT): | 105 - 415 microns |
| Dry Film Thickness (DFT): | 75 - 300 microns |
| Induction Time: | 10 minutes at 23°C |
| Pot Life: | 1.5 hours at 23°C |
| Touch Dry: | 26 hours at -10°C |
| Overcoatable: | 36 hours minimum at -10°C |
| Fully Cured: | 21 days at 0°C |
| Cleaner / Thinner: | Jotun Thinner No. 17 |
| Shelf Life: | 48 months |
| Packaging: | Available in 20 Litres. Off White available in 5 Litres only |