PPG SigmaGuard 260 offers excellent application properties that's ensures you will produce a high quality smooth surface that adheres to the surface supper efficiently.
PPG SigmaGuard 260 should be applied using air or airless spray to produce the best results and a brush should only be used for spot repairs and touch ups. SigmaGuard 260 can be applied at temperatures down to 5°C but faster drying times can be achieved in warmer conditions.
PPG SigmaGuard 260 can be used on steel substrates that are clean, dry and free from any other contamination or paint products. SigmaGuard 260 offers excellent abrasion resistance for when objects or humans come in contact with the surface.
|Type:||High Build Amine Adduct Cured Novolac Phenolic Epoxy|
|VOC Content:||328.0g per Litre|
|Suitable Substrates:||For tank coating|
|Application Method:||Brush, Roller, Air Atomised Spray or Airless Spray|
|Theoretical Coverage:||13.7 m2 per litre at 50 microns|
|Wet Film Thickness (WFT):||95 microns|
|Dry Film Thickness (DFT):||50 microns|
|Induction Time:||10 minutes at 15°C|
|Pot Life:||2 hours at 20°C|
|Touch Dry:||3 hours at 20°C|
|Overcoatable:||Between 8 hours and 1 month at 20°C|
|Fully Cured:||5 days at 20°C|
|Cleaner / Thinner:||PPG Thinner 91-92|
|Shelf Life:||12 months for base and hardener when stored cool and dry|
|Packaging:||Available in 20 Litres|
The manufacturers data sheets are available for download from this website. It is your responsibility to read and understand all aspects of the data sheets before you place an order and prior to application. Please pay special attention to the preparation, mixing and application temperatures of the product, cleaning of substrate and environmental factors such as temperature, rain etc. Quoted coverage rates are based on the manufacturers theoretical rates and may vary depending upon substrates absorption, texture and application. We always recommend a test is carried out to ensure suitability.