Sherwin Williams Transgard TG111V2 - Formerly Leighs

A high build, 2 pack epoxy, zinc phosphate primer buildcoat for the anti corrosive protection of carbon steel surfaces.
Available in 5 Litres
* These colours are for guidance only. Variations between output devices can misrepresent the appearance of an actual colour. Also, we strongly advise that you order your complete paint requirements simultaneously to ensure a uniform batch colour.
3. Select a Qty
As low as:
£146.15
Inc VAT £175.38
PRODUCT DETAILS

Sherwin Williams Transgard TG111V2 - Formerly Leighs is a high build, 2 pack epoxy, zinc phosphate primer buildcoat for the anti-corrosive protection of carbon steel surfaces.

Please note there is a minium order quantity of 150 litres on this product. If you do not require a minimum of this amount, please contact our Technical Team on 01462 421333 to discuss possible alternatives.

Best Uses

Transgard TG111V2 is best used as an anti-corrosive protection of carbon steel surfaces prepared by abrasive blast cleaning. Can be applied at thicknesses between 75 and 150 microns dry to provide both primer and buildcoat in a single coat. A top coat is only required for decorative purposes. For internal and external applications. Excellent resistance to moisture, petroleum solvents, alkali spillagem aliphatic solvents, weather and abrasion.

Application

Blast clean to Sa2½ BS EN ISO 8501-1:2007). Average surface profile in the range 50-75 microns. Manually prepared surfaces should be prepared to a minimum standard of St3 ISO 8501-1:2007 at the time of coating. Ensure surfaces to be coated are clean, dry and free from all surface contamination. May also be applied over a wide range of pre-fabrication primers, including inorganic zinc silicate, and epoxy types. The recommended application method is via airless spray, conventional spray, brush or roller. For overcoating with epoxy products (including self overcoating), the maximum recommended interval is 28 days at 23°C. Where a high degree of gloss and colour retention is required, overcoat with Transgard TG168 or Transgard TG169 within 7 days at a minimum d.f.t. of 50 microns. These overcoating times refer to achievement of optimum adhesion at 23°C and will vary with temperature.

TECHNICAL

Approvals:

  • Highways Agency Item No. 111

Technical Info:

Components: Two Pack
Type: Epoxy Zinc Phosphate Primer
Finish: -
Stock Colours: Light Grey, Red Oxide
Tintable: No
VOC Content: 186 gms/litre
Volume Solids: 75 ± 3%
Suitable Substrates: Carbon Steel
Application Method: Brush, Roller, Airless Spray or Conventional Spray
Theoretical Coverage: 7.5 m2/ltr
Wet Film Thickness (WFT): 133 microns
Dry Film Thickness (DFT): 100 microns
Induction Time: -
Pot Life: 1½ hours at 23°C
Touch Dry: 1½ hours at 23°C
Overcoatable: 4 hours at 23°C
To Handle: 8 hours at 23°C
Cleaner/Thinner No.5 (for thinning), No.9 or No.13 (for cleaning)
Shelf Life: 2 years from date of production unopened or 'use by' date where specified
Packaging: Available in 5 Litres

RELATED PRODUCTS

Navigating through the elements of the carousel is possible using the tab key. You can skip the carousel or go straight to carousel navigation using the skip links.
RODO Paddle Mixer
From £4.38
(£5.26 Inc VAT)
Sherwin Williams Acrolon 7300 Acrylic Finish
Fast-drying, high-gloss PU for long-term exterior gloss and colour retention.
From £108.11
(£129.73 Inc VAT)
Sherwin Williams Transgard TG169 - Formerly Leighs
Fast-drying urethane finish for long-term exterior colour retention.
From £165.14
(£198.17 Inc VAT)
Sherwin Williams Acrolon C137V2 - Formerly Resistex & Transgard TG168
A high quality, fast drying, acrylic urethane exterior gloss. Good colour retention. N9, M24, M34 and No.168. approved.
From £114.32
(£137.18 Inc VAT)