*International Intercure 4500
Please note, this product is now discontinued. See International Intercure 99 for a suitable alternative.
International Intercure 4500 is a low VOC, rapid cure, primer/finish, offering excellent anticorrosive protection and long term aesthetic durability. It replaces the need for alternative two or three coat systems.
Best Uses
Intercure 4500 is ideal for fabrication shops that are looking to reduce heating costs and improve productivity. It is also suitable for facilities that are located in colder climates.
Application
The recommended application method is either Airless Spray or Air Spray (pressure pot). Brush or roller can also be used on small touch up area's only.
Always ensure all surfaces are clean, dry and free from contamination. Prior to application of the paint, all surfaces should be assessed and treated in accordance with ISO 8504:2000.
Oil or grease should be removed in accordance with SSPC-SP1 solvent cleaning.
Steel Substrates
Abrasive blast clean to Sa2½ (ISO 8501-1:2007) or SSPC-SP6. If oxidation has occurred between blasting and application of Intercure 4500, the surface should be re-blasted to the specified visual standard. Any surface defects that are revealed by the blast cleaning process should be ground, filled, or treated in the appropriate manner.
A sharp, angular surface profile of 50-75 microns (2-3 mils) is recommended. Areas of breakdown, damage etc., should be prepared to the specified standard (e.g. Sa2½ (ISO8501-1:2007), or SSPC SP6, abrasive blasting), prior to the application of Intercure 4500.
System Compatibility
Intercure 4500 may be applied direct to metal for atmospheric exposure in environments up to and including C4 (as defined in ISO12944 Part 2). When using Intercure 4500 in C4 environments for high or very high durability periods, a primer will be required. For C5 environments, a primer should always be used.
Suitable primer(s) for ISO 12944 C4 environment are:
Suitable primer(s) for ISO 12944 C5 environment are:
| Components: | Two Component |
| Type: | Direct to Metal Polyaspartic |
| Finish: | Semi-Gloss |
| Stock Colours: | White |
| Tintable: | Limited colour range available. Please note, bespoke tints are non refundable / exchangeable |
| VOC Content: | 225 g/lt |
| Volume Solids: | 77% ± 2% |
| Suitable Substrates: | Steel |
| Application Method: | Airless Spray, Air Spray, Brush, Roller |
| Theoretical Coverage: | 4.40 m²/litre at 175µm d.f.t |
| Wet Film Thickness (WFT): | 195-325µm |
| Dry Film Thickness (DFT): | 150-250µm |
| Induction Time: | - |
| Pot Life: | 1 hour at 25°C |
| Touch Dry: | 30 minutes at 25°C |
| Overcoatable: | Min 2 hours to max 12 months at 25°C |
| Hard Dry: | 2 hours at 25°C |
| Cleaner / Thinner: | International GTA713 (or GTA056) |
| Shelf Life: | 12 months from date of production unopened |
| Packaging: | Available in 20 Litres |