International Intercure 200HS

SKU
id18978
Part A: UN1263 (Class: 3, Pk Grp: III), Part B: UN3470 (Class 8, Pk Grp: II)
Complete with MIO, Intercure 200HS can speed up production and throughput in fabrication shops.
Available in 20 Litres
From £443.16 £369.30
In stock
Only %1 left
Product Description

International Intercure 200HS is a two component, high solids, low VOC, epoxy zinc phosphate / micaceous iron oxide primer offering excellent barrier protection, low temperature cure and rapid overcoating properties.

Best Uses

International Intercure 200HS is best used as a primer for steelwork intended for use in a wide range of environmental conditions including offshore, chemical and petrochemical plants, industrial buildings, pulp and paper mills, power plants and bridges.

It is suitable for overcoating within 7 hours in most climatic conditions hence speeding up production and throughput in fabrication shops. It provides a quick cure even at low temperatures often encountered in maintenance painting.

Application

All surfaces to be coated should be clean, dry and free from contamination. Prior to paint application all surfaces should be assessed and treated in accordance with ISO 8504:2000.

Oil or grease should be removed in accordance with SSPC-SP1 solvent cleaning.

Abrasive Blast Cleaning
Abrasive blast clean to Sa2½ (ISO 8501-1:2007) or SSPC-SP6. If oxidation has occurred between blasting and application of Intercure 200HS, the surface should be reblasted to the specified visual standard.

Surface defects revealed by the blast cleaning process should be ground, filled, or treated in the appropriate manner.

Intercure 200HS is suitable for application to blast cleaned surfaces which were initially to the above standard but have been allowed to deteriorate under good shop conditions for up to 7-10 days. The surface may deteriorate to Sa2 standard but must be free from loose powdery deposits.

A sharp, angular profile of 50-75μm (2-3 mils) should be achieved.

Shop Primed Steel
Weld seams and damaged areas should be blast cleaned to Sa2½ (ISO 8501-1:2007) or SSPC-SP6. If the shop primer shows extensive or widely scattered breakdown overall sweep blasting may be necessary.

Technical Details

Approvals

  • Norsok M-501 System 1 (Pre Qualified)

Intercure 200HS will normally be applied to suitably prepared steel, e.g. blast cleaned. However, if necessary, application over prefabrication blast primers can be performed. Consult International Protective Coatings for further details.

Recommended topcoats/intermediates are:

For other suitable topcoats/intermediates, please consult The Promain Technical Team.

Technical Info

Components: Two Component
Type: Iron Oxide Primer
Finish: Matt
Stock Colours: Sand, Grey, Red
Tintable: No. 
VOC Content: 187 g/lt
Volume Solids: 80%
Suitable Substrates: Steelwork
Application Method: Airless Spray, Air Spray, Brush, Roller
Theoretical Coverage: 5.33 m²/litre at 150 microns d.f.t and stated volume solids
Wet Film Thickness (WFT): 188-250 microns (7.5-10 mils)
Dry Film Thickness (DFT): 150-200 microns (6-8 mils)
Induction Time: -
Pot Life: 90 minutes at 15°C
Touch Dry: 3 hours at 15°C
Overcoatable: After minimum 4 hours at 15°C
Hard Dry: 6 hours at 15°C
Cleaner / Thinner: International GTA220, Clean tools with International GTA220
Shelf Life: 12 months minimum at 25°C (77°F).
Packaging: Available in 20 Litres

The manufacturers data sheets are available for download from this website. It is your responsibility to read and understand all aspects of the data sheets before you place an order and prior to application. Please pay special attention to the preparation, mixing and application temperatures of the product, cleaning of substrate and environmental factors such as temperature, rain etc. Quoted coverage rates are based on the manufacturers theoretical rates and may vary depending upon substrates absorption, texture and application. We always recommend a test is carried out to ensure suitability.

Customer further agrees that Promain have no liability for any errors or omissions contained within the Product Data Sheets and are not liable for failure due to misapplication or inadequate substrate cleaning and preparation. For more information please refer to our Terms & Conditions.

Recommended products to use