Intergard 410 can be used as a primer, a coloured intermediate / undercoat for high performance durable finishes or alternatively, can act as a finish coating where a high quality, decorative finish is not required. Widely used in both new construction and industrial maintenance on offshore structures, chemical plants, power stations and pulp and paper plants.
All surfaces to be coated should be clean, dry and free from contamination. Prior to paint application all surfaces should be assessed and treated in accordance with ISO 8504:2000.
Abrasive Blast Cleaning
Abrasive blast clean to Sa2½ (ISO 8501-1:2007) or SSPC-SP10. If oxidation has occurred between blasting and application of Intergard 410, the surface should be reblasted to the specified visual standard. Surface defects revealed by the blast cleaning process should be ground, filled, or treated in the appropriate manner.
Primed Surfaces
The primer surface should be dry and free from all contamination and Intergard 410 must be applied within the overcoating intervals specified (consult the relevant product data sheet). Areas of breakdown, damage etc., should be prepared to the specified standard (e.g Sa2½ (ISO 8501-1:2007) or SSPC-SP6, Abrasive Blasting, or SSPC-SP11, Power Tool Cleaning) and patch primed prior to the application of Intergard 410.
Shop Primed Steelwork
Weld seams and damaged areas should be blast cleaned to Sa2½ (ISO 8501-1:2007) or SSPCSP10. If the shop primer shows extensive or widely scattered breakdown overall sweep blasting may be necessary.
Metallic Zinc Primed Surfaces
Ensure that the surface of the primer is clean, dry and free from contamination and zinc salts before application of Intergard 410. Ensure zinc primers are fully cured before overcoating.
Intergard 410 can be applied over an extermely wide range of priming systems which include:
Suitable topcoats are:
For other suitable primers / topcoats, consult Promain's technical team.
Components: | Two Part |
Type: | Solvent Based |
Finish: | Semi Gloss |
Stock Colours: | Just tints |
Tintable: | Yes, to a wide range of colours. Please note, bespoke tints are non refundable / exchangeable |
VOC Content: | 338.0g per Litre |
Volume Solids: | 60% |
Suitable Substrates: | Suitable for use as part of a high performance coating system to provide an anti-corrosive barrier in areas where aggressive corrosion conditions prevail. |
Application Method: | Brush, Roller, Air Atomised Spray or Airless Spray |
Theoretical Coverage: | 4.8m2 per litre at 125 microns |
Wet Film Thickness (WFT): | 167 - 250 microns |
Dry Film Thickness (DFT): | 100 - 150 microns |
Induction Time: | - |
Pot Life: | 6 hours at 15°C |
Touch Dry: | 4 hours at 15°C |
Overcoatable: | Between 20 hours and 7 days at 15°C |
Hard Dry: | 20 hours at 15°C |
Cleaner / Thinner: | Thinner: International GTA220. Cleaner: International GTA822 |
Shelf Life: | 12 months minimum at 25°C |
Packaging: | Available in 5 Litres |
The manufacturers data sheets are available for download from this website. It is your responsibility to read and understand all aspects of the data sheets before you place an order and prior to application. Please pay special attention to the preparation, mixing and application temperatures of the product, cleaning of substrate and environmental factors such as temperature, rain etc. Quoted coverage rates are based on the manufacturers theoretical rates and may vary depending upon substrates absorption, texture and application. We always recommend a test is carried out to ensure suitability.