A topcoat for use in atmospheric environments, on a wide range of industrial structures. Replaces Pioner Topcoat.

Available in 5 and 20 Litres in a wide range of colours.

From £80.15 £66.79

In stock

Only %1 left

Skip to the end of the images gallery

Skip to the beginning of the images gallery

Product Details

Product Description

Jotun Pilot ACR is a single component, physically drying acrylic coating, which can be applied direct to metal at sub zero surface temperatures.

Best Uses

Jotun Pilot ACR can be applied directly to metal, at sub-zero surface temperatures. It can be used in both marine and protective environments, and is certified not to spread surface flames.

Good colour and gloss retention
Effective application
Limited waste
Reduces application cost
Direct to metal
Low-temperature drying

Recommended for refineries, power plants, bridges and buildings. Suitable for a wide range of industrial structures. For marine industries, Pilot ACR is ideal for use on topside, superstructure and interiors. More information on Jotun Marine products can be found on the Jotun Marine and Coastal Products page.

Application

The recommended method of application is by airless spray or brush. Care must be taken to achieve the specified dry film thickness. A roller may be used but is not recommended for the first coat on bare metal.

Ensure all surfaces are clean, dry and free from any contamination prior to application.

Surface Preparation Summary Table

Substrate	Minimum	Recommended
Carbon Steel	St 2 (ISO 8501-1)	Sa 2½ (ISO 8501-1)
Galvanised Steel	The surface shall be clean, dry and appear with a rough and dull profile.	Sweep blast-cleaning using non-metallic abrasive leaving a clean, rough and even pattern.
Shop Primed Steel	Clean, dry and undamaged shop primer (ISO 12944-4 5.4)	Clean, dry and undamaged shop primer (ISO 12944-4 5.4)
Coated Surfaces	Clean, dry and undamaged compatible coating	P Sa 2½ (ISO 8501-2)

Technical

Technical Details

Certificates and Approvals

Grain, Newcastle Occupational Health
When used as part of an approved scheme, this material has the following certification:
Low Flame Spread in accordance with EU Directive for Marine Equipment. Approved in accordance with parts 5 and 2 of Annex 1 of IMO 2010 FTP Code, or Parts 5 and 2 of Annex 1 of IMO FTPC when in compliance with IMO 2010 FTP Code Ch. 8

Technical Info

Components:	Single Pack
Type:	Acrylic Coating
Finish:	Semi Gloss
Stock Colours:	White
Tintable:	Yes. Please note, bespoke tints are non refundable / exchangeable
VOC Content:	395 g/l
Volume Solids:	55 ± 2 2%
Suitable Substrates:	Carbon Steel, Galvanised Steel, Coated Surfaces, Shop Primed Steel
Application Method:	Spray, Brush, Roller (roller is not recommended for first coat on bare metal).
Theoretical Coverage:	9.2 - 4.6 m2/L
Wet Film Thickness (WFT):	110 - 220 µm
Dry Film Thickness (DFT):	60 - 120 µm
Induction Time:	-
Pot Life:	-
Touch Dry:	15 minutes at 23°C
Overcoatable:	Minimum 1 hour at 23°C
Walk on Dry:	4 hours at 23°C
Thinner / Cleaner:	Jotun Thinner No. 7 / Jotun Thinner No. 10
Shelf Life:	48 months from date of production unopened
Packaging:	Available in 5 and 20 Litres