Jotun Tankguard SF can be used as primer, mid coat or finish coat in atmospheric and immersed environments. Suitable for properly prepared carbon steel, galvanised steel, stainless steel and concrete substrates. Designed as an internal lining for offshore, onshore and buried tanks and pipes such as chemical storage, waste water, grey water, process water, concrete bund, fire service lines and drilling mud tanks.
For Carbon Steel prepare to Sa 2½ (ISO 8501-1). For Stainless Steel, abrasive blast cleaning to achieve a surface profile using approved non metallic abrasive media which is suitable to achieve a sharp and angular surface profile. For Galvanised Steel: Light brush blasting using non metallic abrasive leaving a clean, rough and even pattern. For Concrete: Dry abrasive blast cleaning to SSPCSP 13/NACE No. 6. for Coated Surfaces: Clean, dry and undamaged compatible coating (ISO 12944-4 6.1).
This product can be applied via airless spray. For stripe coating and small areas apply via brush or roller - see Data sheet.
When applicable, products primarily meant for use as primers or anti-fouling may have slight colour variations from batch to batch. Such products may fade and chalk when exposed to sunlight and weathering.
|Type:||Solvent free amine cured phenolic / novolac epoxy coating|
|Stock Colours:||Buff, Light Grey, Light Red, White|
|VOC Content:||72.0g per litre|
|Suitable Substrates:||Carbon steel, galvanised steel, stainless steel and concrete substrates|
|Application Method:||Airless Spray, Brush or Roller|
|Theoretical Coverage:||6.7 - 2m2 per litre|
|Wet Film Thickness (WFT):||150 - 500 microns|
|Dry Film Thickness (DFT):||150 - 500 microns|
|Induction Time:||10 mins at 23°C|
|Pot Life:||1 hour at 23°C|
|Touch Dry:||15 hours at 10°C|
|Overcoatable:||30 hours at 10°C|
|Fully Cured:||15 days at 10°C|
|Cleaner / Thinner:||Jotun Thinner No. 17|
|Shelf Life:||12 months|
|Packaging:||Available in 15 Litres|
The manufacturers data sheets are available for download from this website. It is your responsibility to read and understand all aspects of the data sheets before you place an order and prior to application. Please pay special attention to the preparation, mixing and application temperatures of the product, cleaning of substrate and environmental factors such as temperature, rain etc. Quoted coverage rates are based on the manufacturers theoretical rates and may vary depending upon substrates absorption, texture and application. We always recommend a test is carried out to ensure suitability.
Customer further agrees that Promain have no liability for any errors or omissions contained within the Product Data Sheets and are not liable for failure due to misapplication or inadequate substrate cleaning and preparation. For more information please refer to our Terms & Conditions.
A one pack coating that contains 96% zinc to provide cold galvanizing cathodic protection of ferrous metals.
A flake filled MIO amine cured epoxy phenolic novolac formulated for use under thermal insulation at elevated or cryogenic temperatures...