RonaBond Crack Bridging Anti-Carbonation Coating WB is a façade coating formulated on a water-based acryl-siloxane. It is used as a waterproof decorative coating and can be applied to most traditional building surfaces after suitable preparation. The addition of siloxane improves shedding of pollutants from the surface and resistance to migration of residues from the substrate. The addition of glass micro-spheres improves application properties and vapour transmission.
RonaBond Crack Bridging Anti-Carbonation Coating WB protects façades against water ingress while allowing improved diffusion of normal levels of moisture vapour from the background provided by inclusion of glass micro-spheres in the formulation. The micro-spheres also provide improved application characteristics. When applied to reinforced concrete it provides excellent protection against corrosion of reinforcement.
Preparation
Prepare the substrate by suitable means (e.g. blasting, high pressure water/grit, scraping, chemical removal) to provide a sound and stable and clean surface; surfaces may be damp but not wet with running water or condensation. Treat surfaces contaminated with moss, algae, fungal growth, etc with RonaBond Fungicidal Treatment or suitable anti-fungal agent such as Centrecoat GS36.
Surface Levelling and Repair Prior To Application
The application of RonaBond Crack Bridging Anti-Carbonation Coating WB (and other paints/coatings) will highlight and exaggerate surface imperfections and undulations. Uneven surfaces may be levelled with RonaBond Easy Skim FC.
Priming
Prime surface with RonaBond Crack Bridging Anti-Carbonation Coating WB diluted with 10% clean water at a rate of 6-7m2 per litre. For high suction backgrounds contact our technical team for advice.
Cracks
Fill fine cracks with RonaBond Stop Crack using a palette knife as appropriate, application should be repeated until the dry crack filler has fully filled the crack.
Application
Apply one or more coats of RonaBond Crack Bridging Anti-Carbonation Coating WB (system dependent) to achieve the specified film thickness and / or dynamic crack accommodation requirement. Apply by RonaBond long-haired roller or airless spray.
A mottled surface texture is a good indicator of adequate spread rate but regular use of a wet film gauge is recommended to ensure the correct coverage. When applying RonaBond Crack Bridging Anti-Carbonation Coating WB 20, RonaBond Crack-bridging Fabric should be pasted into the fresh second layer of RonaBond RonaBond Crack Bridging Anti-Carbonation Coating WB, care should be taken to eliminate bubbles and folds in the fabric.
RonaBond Crack Bridging Anti-Carbonation Coating WB can be applied using airless spray. The nozzle size shall be 625-629. Included within the spray should be a 60 mesh filter. Dilution of the coating can be made with water between 2-10%.
System 2 | System 5 | System 10 | System 20 | |
---|---|---|---|---|
Live crack movement accommodation: | 0.2mm | 0.5mm | 1.0mm | 2.0mm |
1 coat primer (10% diluted coating) at 6-7m2 per litre: | Yes | Yes | Yes | Yes |
1 coat RonaBond Crack Bridging Anti-Carbonation Coating WB at 4m2 per litre: | Yes | |||
2 coats RonaBond Crack Bridging Anti-Carbonation Coating WB @ 4.85m² per litre per coat: | Yes | |||
2 coats RonaBond Crack Bridging Anti-Carbonation Coating WB at 4.0m² per litre per coat: | Yes | |||
2 coats RonaBond Crack Bridging Anti-Carbonation Coating WB at 3.0m² per litre per coat: | Yes | |||
1 layer RonaBond Crack-bridging Fabric: | Yes | |||
1 coat RonaBond Crack Bridging Anti-Carbonation Coating WB at 3.0m² per litre: | Yes |
Components: | Single Pack |
Type: | Water Based Acryl-siloxane dispersion |
Finish: | Matt |
Stock Colours: | Just tints |
Tintable: |
Yes. Colours can be chosen from the Zolpachrom 3 colour range, RonaBond Crack Bridging Anti-Carbonation Coating WB can only be produced in colours with the suffixes PA and ME in the Zolpachrom 3 colour range. Some RAL and BS colours can also be produced, consult our technical department for further information. A light reflectance value of 35 or greater should be chosen for façade coatings. Please note, bespoke tints are non refundable / exchangeable |
VOC Content: | |
Volume Solids: | 69% |
Suitable Substrates: | Masonry. Can be applied on Woodwork and Steel if appropriate primer is used. |
Application Method: | Long Haired Roller or Airless Spray |
Theoretical Coverage: | Between 3m2 and 4.85m2 per litre depending on specification |
Wet Film Thickness (WFT): | |
Dry Film Thickness (DFT): | |
Induction Time: | - |
Pot Life: | - |
Surface Dry: | 2 hours at 20°C |
Overcoatable: | After 24 hours at 20°C |
Fully Cured: | |
Cleaner / Thinner: | Water |
Shelf Life: | Store in frost free conditions away from direct heat and sunlight. Shelf life one year in unopened containers. |
Packaging: | Available in 16 Litres |