Temaprime EE is an anti-corrosive primer for use on steel, aluminium and zinc surfaces. It's many uses include, the interior and exterior of ships above the waterline, agricultural machinery, storage tank exteriors, painting of containers and other steel structures.
All surfaces should be cleaned and dried prior to application.
Steel surfaces should be blast cleaned at least to grade Sa2. Clean small damages by tool cleaning to St2. (ISO 8501-1) If blast cleaning is not possible, phosphating is recommended for cold rolled steel to improve adhesion.
Zinc surfaces should be sweep blast cleaned with mineral abrasives, e.g. quartz sand, to an even roughness. (SaS, SFS 5873) If sweep blasting is not possible, the surface should be roughened by hand abrading or washed with Fonteclean ZN detergent.
Aluminium surfaces should be sweep blast cleaned with non-metallic abrasives to an even roughness. (SaS, SFS 5873) If sweep blasting is not possible, the surface should be roughened by hand abrading or washed with Fonteclean AL detergent.
Primed surfaces should have all oil, grease, salt and dirt removed from the surface by appropriate means. Repair any damage to the primer coat. Note the overcoating time of primer. (ISO 12944-4)
Components: | Single Pack |
Type: | Solvent Based |
Finish: | Matt |
Stock Colours: | Reddish Brown (TVT 4000) and Grey (TVT 4001) |
Tintable: | Yes. Please note, bespoke tints are non refundable / exchangeable |
VOC Content: | 470 g/l |
Volume Solids: | 47 ± 2 % |
Suitable Substrates: | Metal, Galvanised Steel |
Application Method: | Brush, Airless Spray or Conventional Spray |
Theoretical Coverage: | 11m/litre @ 40um |
Wet Film Thickness (WFT): | 85 µm |
Dry Film Thickness (DFT): | 40 µm |
Induction Time: | - |
Pot Life: | - |
Touch Dry: | 1 hour at 23°C |
Overcoatable: | 2 hours at 23°C |
Cleaner / Thinner: | Thinners 1006 and 1053 |
Shelf Life: | See tin for shelf life and storage information |
Packaging: | Available in 3 and 10 Litres |