Zinga Aluspray is best used as an aesthetic RAL 9006 aluminium coloured topcoat for existing Zinga coats, a metallisation layer, or without a primer on to an old, non corroded hot dip galvanisation.
Aluspray can be applied on ferro-metals and (damaged) zinc surfaces.For optimal performance, the metal should first be degreased, preferably by steam-cleaning. Alternatively, the surface can be degreased using solvent (e.g. Zingasolv). Never use white spirit. - For optimal performance, clean to SA 2,5 (ISO 8501:2007). For non-critical (small) areas, cleaning to St 3 is sufficient (using a steel brush). Apply the Aluspray as soon as possible on the prepared metal substrate (max. 4 hours waiting time).
|Stock Colours:||Aluminium comparable to hot dip galvanization|
|VOC Content:||619.0g per Litre|
|Suitable Substrates:||For without primer on an old, non-corroded hot-dip galvanisation or metallisation layer or as topcoat on top of ZINGA 96%.|
|Theoretical Coverage:||4 m2 per litre at 40 microns|
|Wet Film Thickness (WFT):|
|Dry Film Thickness (DFT):||40 microns|
|Touch Dry:||15 minutes at 20°C for 40 microns|
|Overcoatable:||Always apply 2 layers, apply the second coat 1 hour after touch dry|
|Fully Cured:||48 hours at 20°C for 40 microns|
|Cleaner / Thinner:||-|
|Shelf Life:||2 years unopened|
|Packaging:||Available in 500ml Aerosols|
The manufacturers data sheets are available for download from this website. It is your responsibility to read and understand all aspects of the data sheets before you place an order and prior to application. Please pay special attention to the preparation, mixing and application temperatures of the product, cleaning of substrate and environmental factors such as temperature, rain etc. Quoted coverage rates are based on the manufacturers theoretical rates and may vary depending upon substrates absorption, texture and application. We always recommend a test is carried out to ensure suitability.
Customer further agrees that Promain have no liability for any errors or omissions contained within the Product Data Sheets and are not liable for failure due to misapplication or inadequate substrate cleaning and preparation. For more information please refer to our Terms & Conditions.
A one pack coating that contains 96% zinc to provide cold galvanizing cathodic protection of ferrous metals.
A zinc rich coating formulated as an easily applied, cold galvanising protector against corrosion on all ferrous metals.