Zinga Zingaspray, 500ml Aerosol

SKU
id12541
UN1950 (Class: 2.1)
Zinga 500ml 96% Zinc aerosol with all the protection of Zinga 96% Zinc Cathodic Protection.
Available in 500ml Aerosols
£19.92 £16.60
In stock
Product Description

Zinga's Zingaspray is a convenient 500ml aerosol with all the advantages of Zinga 96% Zinc Cathodic Protection in a simple hand held can.

Best Uses

Zingaspray aersols are best used for repairing worn or damaged hot dip galvanising or spot repair on items previously coated with Zinga 96% Zinc Cathodic Protection. Zingaspray aersols offer cold galvanizing paint protection of ferrous metal structures as an alternative to hot dip galvansation or metallisation.

Preparation

For Marine Structures: Remove all growth with a UHP water jet or high pressure wash down. Leave to dry. Blast clean the substrate.

For Old or Worn Galvanising or Repair of Old Zinga: Steam clean to remove contamination from porous surfaces, dry off, blast clean as normal.

For New Steel: Steam clean or high pressure wash down all surfaces. Leave to dry. Blast clean to standard Sa 2.5

New Galvanised Steel: Steam clean substrate. Sweep blast the surface at a blast pressure of 55psi using a 45° nozzle angle to avoid removing any existing zinc thickness.

For Cast Iron: Steam clean or high pressure wash down all surfaces. Leave to dry. Blast clean to standard Sa 2.5

For Aluminium Alloys: Solvent clean as per SSPC-SP1 Standard. Blast clean with aluminium oxide media grade 3. Vacuum surface before application.

Application

One coat of Zingaspray will dry at approximately 20-25 microns. Therefore a minimum of two coats is recommended.

Technical Details

Notes

  • Zinga aersols are suitable for the repair of worn or damaged hot dip galvanising or spot repair on items previously coated with Zinga 96% Cathodic Protection.

Technical Info

Components: One Part
Type: Aerosol
Finish: Matt
Stock Colours: Grey
Tintable: No
VOC Content: 668.0g per Litre
Volume Solids: 16.8%
Suitable Substrates: For the repairing and touching-up of damaged or old hot-dipped, Zinganised or other zinc coated structures.
Application Method: Aerosol
Theoretical Coverage: 4.22 m2 per litre at 40 microns
Wet Film Thickness (WFT): -
Dry Film Thickness (DFT): 40 microns
Induction Time: -
Pot Life: -
Touch Dry: 15 minutes at 20°C in 40 microns
Overcoatable: Always apply 2 layers, apply the second coat 1 hour after touch dry.
Fully Cured: 48 hours at 20°C in 40 microns
Cleaner / Thinner: -
Shelf Life: 2 years unopened
Packaging: Available in 500ml Aerosols
Product Video

The manufacturers data sheets are available for download from this website. It is your responsibility to read and understand all aspects of the data sheets before you place an order and prior to application. Please pay special attention to the preparation, mixing and application temperatures of the product, cleaning of substrate and environmental factors such as temperature, rain etc. Quoted coverage rates are based on the manufacturers theoretical rates and may vary depending upon substrates absorption, texture and application. We always recommend a test is carried out to ensure suitability.

Customer further agrees that Promain have no liability for any errors or omissions contained within the Product Data Sheets and are not liable for failure due to misapplication or inadequate substrate cleaning and preparation. For more information please refer to our Terms & Conditions.

Recommended products to use