Macropoxy M111 is suitable for application to surfaces which have been prepared by wet abrasive blasting. May also be applied to grit blasted surfaces and for surfaces prepared by UHP water blasting where existing blast profile is exposed. Tolerant to application to surfaces which may be damp or wet at the time of application. An acceptable ‘ wet ‘ surface is defined as a surface on which a thin film of moisture is present, but is free from running water, droplets or pooled water.
Dry abrasive blast to Sa2½ BS EN ISO 8501-1:2007. Average surface profile in the range 50-75 microns. UHP or Aquagrit water blasted surfaces must also reveal an underlying surface equivalent to Standard Wa2½ (BS EN ISO 8501-4:2006). Light flash rust staining (as defined in Section 6 BS EN ISO 8501-4:2006) is acceptable provided it cannot be removed by rubbing. Manually prepared surfaces are acceptable for non-immersed situations and should be prepared to a minimum standard of ST3 BS EN ISO 8501-1:2007 and must be clean, dry and free from all surface contamination at the time of coating.
Recomended application method is via airless spray, conventional spray or brush. Recommended thinner Sherwin Williams Thinner No 5. Indefi nitely overcoatable with epoxy systems provided the surfaces to be coated have been suitably cleaned. Where a high degree of gloss and colour retention is required overcoat with Acrolon C137V2, Acrolon C237, Acrolon 1850 and Acrolon 7300 within 7 days at a minimum dft of 50 microns or in the case of Acrolon C750V2 overcoat within 4 days. These overcoating times refer to achievement of optimum adhesion at 23°C and will vary with temperature.
|Type:||Epoxy zinc phosphate primer|
|Stock Colours:||Red Oxide|
|VOC Content:||383 gms/litre|
|Volume Solids:||54 ± 4%|
|Suitable Substrates:||For application to surfaces which have been prepared by wet abrasive blasting|
|Application Method:||Brush, Airless Spray or Conventional Spray|
|Theoretical Coverage:||10.8 m2/lt|
|Wet Film Thickness (WFT):||93 microns|
|Dry Film Thickness (DFT):||50 microns|
|Pot Life:||8 hours at 23°C|
|Touch Dry:||15 minutes at 23°C|
|Overcoatable:||4 hours at 23°C|
|To Handle:||16 hours at 23°C|
|Cleaner / Thinner:||Thinner No.5|
|Shelf Life:||12 months from date of production unopened or 'use by' date where specified|
|Packaging:||Available in 5 Litres and 20 Litres|
The manufacturers data sheets are available for download from this website. It is your responsibility to read and understand all aspects of the data sheets before you place an order and prior to application. Please pay special attention to the preparation, mixing and application temperatures of the product, cleaning of substrate and environmental factors such as temperature, rain etc. Quoted coverage rates are based on the manufacturers theoretical rates and may vary depending upon substrates absorption, texture and application. We always recommend a test is carried out to ensure suitability.
Customer further agrees that Promain have no liability for any errors or omissions contained within the Product Data Sheets and are not liable for failure due to misapplication or inadequate substrate cleaning and preparation. For more information please refer to our Terms & Conditions.
A high performance fast drying acrylic urethane sheen finish for use where long term exterior colour retention characteristics are requ...
A self curing solvent based zinc silicate coating for the protection of blast cleaned steel surfaces up to 400°C.
A two pack isocyanate free finish based on an acrylic epoxy binder system. NORSOK M501 Rev 6 System 1.
A high performance, fast drying, acrylic urethane exterior gloss with good colour retention. N9, M24, M34 and Item No.168. approved.