Jotun Jotatemp 1000
Jotun Jotatemp 1000 is designed as a heat-resistant coating - it is resistant to low temperatures down to -196°C and high temperatures up to 1000°C continuously, where substrates allow. Can be used as primer or finish coat in atmospheric environments.
Best Uses
Jotun Jotatemp 1000 is a three component titanium catalyzed inorganic ceramic copolymer based coating, which cures in ambient conditions. It complies to the generic type inert multipolymeric matrix coating.
Suitable for properly prepared carbon steel and ceramic substrates, Jotun Jotatemp 1000 can be applied on hot substrates up to 250°C. Please refer to the application guide for more detailed information. It will offer proper corrosion protection at ambient conditions during construction and shut-down periods. The product passes the standard tests used for qualifying coatings preventing corrosion under insulation (CUI).
Suitable for insulated and non-insulated surfaces of carbon steel and ceramic substrates. Specially designed for preventing corrosion under insulation (CUI) above 250°C. Can be used in combination with Jotun Jotatemp 540 Zinc as primer, providing heat resistance up to 540 °C and lasting corrosion protection. For optimized performance on stainless steel and alloyed steel (P91), we recommend Jotun Jotatemp 1000 HT.
Application
Preparation
- Carbon steel - Sa 2½ (ISO 8501-1).
- Ceramic substrates - The surface should be clean and dry
- Coated surfaces - Clean, dry and undamaged compatible coating
Application
The product can be applied by airless spray. Brush is recommended for stripe coating and small areas. Care must be taken to achieve the specified dry film thickness. Follow Application Guide for full information.
Approvals and Certifications
- Tested in accordance with ISO 12944-6, high expected durability in corrosivity category C5
- Passing vertical pipe test for CUI performance as described in ISO 19277-2018
- Passing 1000 hours dry heat test at 540°C on carbon steel
- Passing 1000 hours dry heat test at 1000°C on ceramic substrates
- Passing ASTM D2485 : 2018 - Standard Test Methods for Evaluating Coatings For High Temperature Service
- Passing ASTM D6944 : 2009 - Resistance of cured coatings to thermal cycling
Technical Info
| Components: | Three Part |
| Type: | Titanium catalyzed inorganic ceramic copolymer |
| Finish: | Matt |
| Stock Colours: | Dark grey, aluminium, aluminium effect (close to RAL 9006) |
| Tintable: | No |
| VOC Content: | 300.0g per Litre |
| Volume Solids: | 75% |
| Suitable Substrates: | Suitable for insulated and non-insulated surfaces of carbon steel and ceramic substrates |
| Application Method: | Airless Spray, Brush |
| Theoretical Coverage: | 5 - 7.5 m2 per litre |
| Wet Film Thickness (WFT): | 130 - 200 microns |
| Dry Film Thickness (DFT): | 100 - 150 microns |
| Induction Time: | |
| Pot Life: | 10 hours at 10°C |
| Touch Dry: | 5.5 hours at 10°C |
| Overcoatable: | 24 hours at 10°C |
| Fully Cured: | 4 days at 10°C |
| Cleaner / Thinner: | Jotun Thinner No. 7 / Jotun Thinner No. 10 |
| Shelf Life: | 24 months for comp B and C, 12 months for comp A |
| Packaging: | Available in 4.54 Litres |