Teamac P218 Rapidry Hi-Build Zinc Phosphate Primer
Teamac Rapidry HB Zinc Phosphate Primer is a high build, high performance quick drying metal primer. It has excellent anti-corrosive properties.
Best Uses
Teamac Rapidry HB Zinc Phosphate Primer is used as an anti-corrosive primer on iron and steel where rapid coating and finishing is required. Ideal in coastal areas. With exceptional anti-corrosive properties, Teamac's Rapidry High Build Zinc Phosphate Primer is suitable for external iron and steel protection against the elements.
Available in a semi matt finish in red and grey.
Application
Ensure all surfaces are clean, dry and free from grease, oil and any other contaminates. Bare steel should be free from dust, rust and scale. Blast cleaning to SA 2½ is recommended. If blast cleaning is impractical, mechanical cleaning should be employed as hand cleaning does not clean the steel to the required degree. Any oil or grease should be removed with Teamac Universal Degreaser before de-rusting. Where blast cleaning is carried out after assembly, special attention must be paid to edges, corners, nuts, bolts, welds etc. Welds should, if necessary be ground and all weld spatter, slag etc. must be removed.
| Components: | One Part |
| Type: | Solvent Based |
| Finish: | Semi Matt |
| Stock Colours: | Red, Black, Cream and Grey |
| Tintable: | No |
| VOC Content: | 470.0g per Litre |
| Volume Solids: | 45% |
| Suitable Substrates: | For iron and steel |
| Application Method: | Airless Spray |
| Theoretical Coverage: | 10 m2 per litre at 45 microns |
| Wet Film Thickness (WFT): | 100 microns |
| Dry Film Thickness (DFT): | 45 microns |
| Induction Time: | - |
| Pot Life: | - |
| Touch Dry: | 30 minutes at 20°C |
| Overcoatable: | After 4 hours at 20°C |
| Fully Cured: | - |
| Cleaner / Thinner: | Teamac Thinners V/607/16 |
| Shelf Life: | 2 years unopened in original packaging |
| Packaging: | Available in 5 Litres |