International Ceilcote 232 Flakeline

International Ceilcote 232 Flakeline is a flake filled coating that offers outstanding chemical resistance with quick turn around for service and also high temperature resistance. Uses Ceilcote No.2 Hardener.

Best Uses

Ceilcote 232 Flakeline is intended for use on tanks or other steel structures, trenches, pits, secondary containment and floors, where chemical resistance is the primary concern.

Typical application area's include:

• FGD raw and treated gas ducts
• Gas to gas heat exchangers
• Process equipment such as separators, coalescers, knock out drums, absorbers, feed tanks and clarifiers

Application

The recommended application is via Airless Spray. Brush or roller are also suitable, however, multiple coats may be required to achieve specified film thickness. 

All surfaces to be coated should be clean, dry and free from contamination. Prior to paint application all surfaces should be assessed and treated in accordance with ISO 8504:2000.

Oil or grease should be removed in accordance with SSPC-SP1 solvent cleaning.

Steel Substrates
For immersion service or service in humid conditions or elevated temperatures, this product should be applied to surfaces which have been prepared by abrasive blast cleaning to Sa3 (ISO 8501-1:2007), SSPC SP5 or NACE #1. For dry environments, abrasive blast cleaning to Sa2½ (ISO 8501-1:2007), SSPC SP10 or NACE #2 will be suitable. A sharp, angular surface profile of 75 microns (3 mils) is recommended.

Concrete Substrates
Concrete should be well cured prior to priming with the appropriate primer. The concrete surface should be dry and pass the plastic sheet test (ASTM D4263). All surfaces should be clean, dry and free from curing compounds, release agents, trowelling compounds, surface hardeners, efflorescence, grease, oil, dirt, old coatings and loose or disintegrating concrete.

All concrete surfaces must also be abrasive blast cleaned to provide a roughened surface and remove laitance. The surface tensile strength (ASTM 4541) as prepared should be at least 2MPa (300 psi). Refer to the Concrete Surface Preparation Guidelines for more information.

Surfaces must be primed using Ceilcote 380 Primer at 50-125 microns WFT (2-5 mils WFT).