International Interbond 2340UPC

SKU
id23926
Parts A & B: UN1263 (Class: 3, Pk Grp: III)
A universal pipe coating that provides external protection for process piping, valves and vessels.
Available in 20 Litres
From £706.16 £588.47
In stock
Only %1 left
Product Description

International Interbond 2340UPC is a high temperature pipe coating that provides corrosion resistance in accordance with the ISO 12944-9 standard at ambient temperatures.

Best Uses

Interbond 2340UPC is suitable for use on both carbon steel and stainless, both insulated and uninsulated, as well as cryogenic service. It can be used on both new construction and maintenance repair.

Interbond 2340UPC has excellent resistance to 'thermal shock' experienced during rapid temperature cycling.

Application

The recommended application method is Airless Spray. Brush or roller can be used on smaller areas only. Please note, this product is not suitable for use with Conventional Sprays.

Ensure all surfaces are clean, dry and free from contamination. Prior to application, all surfaces should be assessed and treated in accordance with ISO 8504:2000. Oil or grease should be removed in accordance with SSPC-SP1 solvent cleaning.

New Construction
For optimum performance and in new construction phase, Interbond 2340UPC should be applied to abrasive blast cleaned steel, minimum Sa2½ (ISO 8501-1:2007) or SSPC SP10. A sharp, angular surface profile of 50-75 microns (2-3 mils) is recommended.

Apply Interbond 2340UPC before oxidation occurs. If oxidation does occur, the entire oxidised area should be re-blasted to the standard specified. Any surface defects that are revealed by the blast cleaning process should be ground, filled, or treated in the appropriate manner. For small areas of touch up repair and welds, power tool cleaning to SSPC SP11 is suitable.

Optimum performance will be achieved with a minimum surface profile of 50 microns (2 mils).

Maintenance & Repair
For on-site planned maintenance and repair in some service conditions, Interbond 2340UPC may be applied to bare steel substrates prepared to a minimum of St2 (ISO 8501-1:2007). See application guidelines for further information.

Austenitic Stainless Steel
Ensure the surface is clean, dry and free from metal corrosion products prior to application. Abrasive blast with non-metallic and chloride free abrasive (e.g. aluminium oxide or garnet) to obtain an average anchor profile of 35 microns (1.4 mils).

System Compatibility

Interbond 2340UPC is normally applied direct to metal and is compatible with a number of topcoats.

Technical Details

Features and Benefits

  • Two component coating delivering temperature resistance and corrosion protection from -196°C (-321°F) to 230°C (450°F)
  • Provides protection against corrosion under insulation (CUI)
  • Excellent tolerance to over application
  • Low temperature cure down to -5°C (23°F)
  • Short minimum overcoating intervals
  • Suitable for hot application up to 120°C (248°F)

Technical Info

Components: Two component
Type: Universal Pipe Coating
Finish: Semi-Gloss
Stock Colours: Grey, Pink, Olive Grey
Tintable: Other colours regionally available. Please contact us for more information.
VOC Content: 390 g/lt
Volume Solids: 60%
Suitable Substrates: Carbon Steel, Stainless Steel
Application Method: Airless Spray, Brush, Roller
Theoretical Coverage: 3 m²/litre at 200µm d.f.t
Wet Film Thickness (WFT): 167-333µm
Dry Film Thickness (DFT): 100-200µm
Induction Time: -
Pot Life: 3 hours at 20°C
Touch Dry: 4 hours at 20°C
Overcoatable: Min 7 hours to max 14 days at 20°C
Hard Dry: 6 hours at 20°C
Cleaner / Thinner: International GTA220
Shelf Life: 12 months from date of production unopened
Packaging: Available in 20 Litres