Jotun Barrier is a 2 pack low film build anti-corrosive epoxy mastic for application to steel. A zinc rich aluminium finish epoxy primer, Jotun Barrier is part of the Highways Approved paint system but is also suitable for use on steel vessels above or below the water line.
When applying Barrier below the waterline it is recommended that either the aluminium or re-toned colour should be applied. Highways Agency Item No.109.
Jotun Barrier is suitable for structural steel and piping which is exposed to corrosive environments. It is recommended for offshore environments, refineries, power plants, bridges, buildings, mining equipment and generral structural steel. Jotamastic Barrier is designed as a primer in coating systems where extended durability is essential.
Jotun Barrier complies with the compositional requirements for SSPC Paint 20 level 2 and ISO 12944. Barrier is supplied with ASTM D520 Type II zinc dust.
Jotun Barrier is suitable for application to manually prepared and sand blasted surfaces making this surface tolerant paint suitable for areas that are difficult to prepare. When applying in marine environments, it is recommended that a minimum of 2 coats of Jotamastic Barrier is applied above the water line and 3 coats to areas below the water.
Surface and Environment
Jotun Jotamastic Barrier is for structural steel and piping which is exposed to high corrosive environments.
- Part of Network Rail/Railtrack RT98 system M20 and N4
- Certificates XM92/M20-140 and XN90/N4-077
- Highways Agency Item No.109
- Low Flame Spread in accordance with EU Directive for Marine Equipment. Approved in accordance with parts 5 and 2 of Annex 1 of IMO 2010 FTP Code, or Parts 5 and 2 of Annex 1 of IMO FTPC when in compliance with IMO 2010 FTP Code Ch. 8
- Pre-qualification testing in accordance with NORSOK M-501, Rev. 5, System 1, suitable for exterior exposure in offshore environment, below 120 °C.
|Type:||Polyamide cured zinc rich epoxy coating|
|VOC Content:||475.0g per litre|
|Suitable Substrates:||Carbon steel, repair of inorganic zinc silicate coating and damaged galvanised steel substrates.|
|Application Method:||Airless Spray or Brush|
|Theoretical Coverage:||2.12 - 4.2m2 per litre|
|Wet Film Thickness (WFT):||45 - 235 microns|
|Dry Film Thickness (DFT):||25 - 125 microns|
|Induction Time:||30 mins at 23°C|
|Pot Life:||24 hours at 23°C|
|Touch Dry:||20 mins at 10°C|
|Overcoatable:||2 hours at 10°C|
|Fully Cured:||7 days at 10°C|
|Cleaner / Thinner:||Jotun Thinner No. 17|
|Shelf Life:||24 months|
|Packaging:||Available in 4 and 9 Litres|
The manufacturers data sheets are available for download from this website. It is your responsibility to read and understand all aspects of the data sheets before you place an order and prior to application. Please pay special attention to the preparation, mixing and application temperatures of the product, cleaning of substrate and environmental factors such as temperature, rain etc. Quoted coverage rates are based on the manufacturers theoretical rates and may vary depending upon substrates absorption, texture and application. We always recommend a test is carried out to ensure suitability.
Customer further agrees that Promain have no liability for any errors or omissions contained within the Product Data Sheets and are not liable for failure due to misapplication or inadequate substrate cleaning and preparation. For more information please refer to our Terms & Conditions.