Jotun Penguard WF is a two component water borne epoxy coating for corrosion protection. Especially designed for new construction where short dry to handle and over coating times are required.
Jotun Penguard WF is formulated to be used as primer, mid coat, finish coat or as single coat system in atmospheric environments. This product is a versatile, fast drying product containing flash rust inhibitors. It cures down to 5°C. Specially designed for new construction where short dry to handle and over coating times are required. Can be used as primer, mid coat, finish coat or as single coat system in atmospheric environments. Suitable for properly prepared carbon steel, aluminium, concrete and galvanised steel substrates. Available with hardener for application at low substrate temperatures.
Suitable for structural steel and piping to be exposed to corrosive environments up to high. Recommended for offshore environments, refineries, power plants, bridges, buildings and mining equipment. Suitable for over coating with water borne acrylics, water borne epoxy and suitable solvent borne coatings.
For Carbon Steel, prepare to Sa2.5. For Aluminium, abrasive blast clean to achieve a surface profile using approved non metallic abrasive media which is suitable to achieve a sharp and angular surface profile. For Galvanised Steel, light brush blast using non metallic abrasive leaving a clean, rough and even pattern. For concrete, allow a minimum 4 weeks curing. Moisture content maximum 5%. Prepare the surface by means of enclosed blast shot or diamond grinding and other appropriate means to abrade the surrounding concrete and to remove laitance.
Apply using airless spray. A brush is recommended for stripe coating and small areas, care must be taken to achieve the specified dry film thickness. Rollers may be used for small areas but is not recommended for first primer coat. However, when using roller application care must be taken to apply sufficient material in order to achieve the specified dry film thickness.
Contributes to satisfying the following credit(s):
- Indoor Environmental Quality (IEQ) under LEED® 2009
- Environmental Quality (EQ) and Materials and Resources (MR) under LEED® v4
- Meets VOC content requirements for BREEAM® International and BREEAM® NOR.
- Meets VOC content requirements for Estidama
- Meets VOC content requirements for GSAS
- Meets requirements for China Environmental Label
- Fire test approved for use under Jotun Steelmaster 1200WF
|Type:||Water borne epoxy coating|
|Stock Colours:||Grey XO and Red|
|VOC Content:||65.0g per Litre|
|Suitable Substrates:||Suitable for properly prepared carbon steel, aluminium, concrete and galvanised steel substrates.|
|Application Method:||Airless Spray. Brush or Roller for Small Areas or Stripe Coats|
|Theoretical Coverage:||3.4 - 6.8 m2 per litre|
|Wet Film Thickness (WFT):||145 - 295 microns|
|Dry Film Thickness (DFT):||75 - 150 microns|
|Induction Time:||15 mins at 23°C|
|Pot Life:||1.5 hours at 23°C|
|Touch Dry:||1.5 hours at 23°C|
|Overcoatable:||4.5 hours at 23°C|
|Fully Cured:||7 days at 23°C|
|Cleaner / Thinner:||Thinner: Water. Cleaner: Jotun Thinner No. 17 or Jotun Thinner No. 4|
|Shelf Life:||12 months for Part A, 24 months for Part B|
|Packaging:||Available in 15 Litres|
The manufacturers data sheets are available for download from this website. It is your responsibility to read and understand all aspects of the data sheets before you place an order and prior to application. Please pay special attention to the preparation, mixing and application temperatures of the product, cleaning of substrate and environmental factors such as temperature, rain etc. Quoted coverage rates are based on the manufacturers theoretical rates and may vary depending upon substrates absorption, texture and application. We always recommend a test is carried out to ensure suitability.