PPG PhenGuard 965 is a two component, high build, amine adduct-cured novolac phenolic epoxy coating for offshore, marine and chemical / petrochemical sectors.
PPG PhenGuard is formulated as a chemical resistant tank lining. For detailed information on resistance and resistance notes please contact us.
- Excellent resistance to a wide range of organic acids, alcohols, fats (regardless of free fatty acid content) and solvents
- Maximum cargo flexibility
- Low cargo absorption
- Easy to clean
- Good resistance to hot water
- Can be applied and cures at temperatures down to 5°C (41°F)
- Good application properties, resulting in a smooth surface
Steel should be blast cleaned in situ to at least ISO 2 1/2 with a blasting profile of between 50-100 microns. Steel mist be free from rust, scale, shop primer and any other contamination. Please allow for tins induction time of 10 minutes at 15°C.
Minimum curing time of PhenGuard 965 system before transport of cargoes is 3 months according to datasheet. For transport of methanol and vinyl acetate monomer, a hot cure is required which cannot be substituted by a service period of 3 months with non aggresive cargoes. Adequate ventilation must be maintained during application and curing. When used as a primer under solvent free tank linings, the DFT must be limited to a maximum of 100 microns (4 mils).
|Stock Colours:||Off White, Pink, Grey|
|VOC Content:||329.0 g/l|
|Application Method:||Air or Airless Spray|
6.8m2 per litre for 100 microns
5.4m2 per litre for 125 microns
|Wet Film Thickness (WFT):|
|Dry Film Thickness (DFT):||500 - 1500μm|
|Pot Life:||2 hours at 20°C|
|Touch Dry:||18 hours at 1500 microns at 20°C|
|Recoatable:||8 hours - 14 days at 20°C|
|Full Cure||3 days at 20°C|
|Cleaner / Thinner:||Clean with PPG Thinner 91-92|
|Shelf Life:||At least 12 months when stored cool and dry|