Sherwin Williams Transgard TG115 - Formerly Leighs

Product Description

Sherwin Williams Transgard TG115 - Formerly Leighs is a high build aluminium epoxy maintenance primer for abraded surfaces.

Best Uses

Sherwin Williams Transgard TG115 is best suited for brush application onto hand or mechanically prepared surfaces giving excellent wetting and adhesion characteristics. Suitable for atmospherically exposed surfaces but not recommended for exposure to severe chemical environments. May be spray applied to blast cleaned surfaces. Recommended curing temperature above 10°C. Extended drying times will be observed at lower temperatures. Macropoxy M902 is recommended alternative for low temperature application and curing.

Application

Recommended application via brush or airless spray onto blast cleaned surfaces. Recommended cleanser / thinner no5 for thinning, no9 or no13 for cleaning. Recommended undercoat Transgard TG116. For overcoating with epoxy products (including self overcoating), the maximum recommended interval is 28 days at 23°C. Blast clean to Sa2½ BS EN ISO8501-1:2007. Average surface profile in the range 50-75 microns. Manually prepared surfaces should be prepared to a minimum standard of ST3 BS EN ISO8501-1:2007 at the time of coating. Ensure surface to be coated are clean, dry and free from all surface contamination. Compatibility - This product is fully compatible with Epigrip M902 ( Item 115 low temperature curing grade ) and the two products may be interchanged within any specification requiring the use of Item 115, depending upon the application conditions.

Technical Details

Approvals:

• Highways Agency Item No.115

Technical Info:

• Drying Times: 6 hours at 15°C to touch, 16 hours at 15°C to recoat
• Dry Film Thickness: 100 microns
• Theoretical Coverage: 7.5m2 per litre
• Pot Life: 3 hours at 15°C
• Available Colour: Aluminium
• Available in 5 Litres