*Jotun Marathon 1000 GF
Please note, this product is now discontinued. Contact our technical team for a suitable alternative.
Jotun Marathon 1000 GF is a two component polyamine cured epoxy coating that is high build, solvent free, and glass flake reinforced coating for marine environments.
Best Uses
Jotun Marathon 1000 GF provides very good impact and abrasion resistance. Suitable for environments with very high corrosivity, such as areas in the splash or tidal zone. Can be used as primer, mid coat, finish coat or as single coat system in atmospheric and immersed environments. Suitable for properly prepared carbon steel substrates.
Jotun Marathon 1000 GF is suitable for structural steel and piping to be exposed to corrosive environments up to very high and immersed. Recommended for offshore environments, refineries, power plants, bridges, buildings, mining equipment and general structural steel. Specially suited in areas where high mechanical strength is required, such as splash or tidal zones.
Can be used as a non-slip deck system in combination with appropriate anti-skid aggregate and finish coat. Compatible with cathodic protection systems.
Application
Preparation
- Carbon steel - Sa 2½ (ISO 8501-1)
- Shop primed steel - Sweep blasted or alternatively blasted to Sa 2 (ISO 8501-1) of at least 70% of the surface.
- Coated surfaces - Clean, dry and undamaged compatible coating
The product can be applied by airless spray, or two component heated airless spray equipment. Brush application is recommended for stripe coating and small areas. Care must be taken to achieve the specified dry film thickness. Follow Application Guide sheet.
Approvals and Certifications
- NORSOK Standard M-501, Edition 6, Coating system no. 1 - Carbon steel with maximum operating temperature <120°C
- NORSOK Standard M-501, Edition 6, Coating system no. 4 - Walkways, escape routes and lay down areas
- NORSOK Standard M-501, Edition 6, Coating system no. 7A - Carbon and stainless steel in the splash zone
Technical Info
| Components: | Two Pack |
| Type: | Polyamine cured epoxy |
| Finish: | |
| Stock Colours: | Range of Stock Colours |
| Tintable: | No |
| VOC Content: | 47g per Litre |
| Volume Solids: | 98% |
| Suitable Substrates: | Structural Steel |
| Application Method: | Airless Spray, Brush |
| Theoretical Coverage: | 1 - 2 m2 per litre |
| Wet Film Thickness (WFT): | 510 - 1020 microns |
| Dry Film Thickness (DFT): | 500 - 1000 microns |
| Induction Time: | - |
| Pot Life: | 45 minutes at 23°C |
| Touch Dry: | 10 hours at 15°C |
| Overcoatable: | 16 hours minimum at 15°C |
| Fully Cured: | 10 days at 15°C |
| Cleaner / Thinner: | Jotun Thinner No. 17 |
| Shelf Life: | 12 months |
| Packaging: | Available in 18 Litres |