Bradite Surface Tolerant Primer EP92 is a two pack polymide adduct cured primer, for steel substrates, containing a high level of zinc phosphate anti-corrosive pigment.

Best Uses

Bradite Surface Tolerant Primer EP92 is used as a surface tolerant anti-corrosive epoxy primer which is capable of being applied over lightly rusted ferrous surfaces. It is ideally suited for surfaces and structures on which thorough blast cleaning may not be feasible or practical.

Application

Preparation – industrial protective coating

High pressure steam cleaning to remove all loose, flaking paint and contamination back to a sound surface. Bradite TD39 industrial strength detergent, washing and rinsing should be used with scrubbing to remove grease or oil.

For new or total repair, steel should be blast cleaned to SIS Sa 21/2 minimum with a blast profile of 35-50 microns. (For maintenance repair, sweep blast or mechanically abrade existing coating to provide a key. Damaged or rusty areas should be blast cleaned to SIS Sa 21/2 or mechanically abraded to SIS St 3 minimum).

1st coat Bradite Surface Tolerant Epoxy Primer EP92*
2nd coat Bradite HB MIO Epoxy Build Finish EM97
3rd coat Bradite Polyurethane Gloss Finish PG77
4th coat Bradite Polyurethane Gloss Finish PG77

For maintenance painting the 1st coat will be a touch up to bare areas only.


Preparation – wet blasted steel

High pressure steam cleaning to remove all loose, flaking paint and contamination back to a sound surface. Bradite TD39 industrial strength detergent, washing and rinsing should be used with scrubbing to remove grease or oil. Steel should be wet blast cleaned to SIS Sa 21/2 minimum with a blast profile of 35-50 microns then rinsed
with fresh water, with excess water being blown off with oil free compressed air. (For maintenance repair, wet blast as previous, feather existing coating to a sound edge and abrade to provide a key.)

Painting System

1st coat Bradite Surface Tolerant Epoxy Primer EP92
2nd coat Bradite HB MIO Epoxy Build Finish EM97
3rd coat Bradite Polyurethane Gloss Finish PG77

For maintenance painting the 1st coat will be a touch up to bare areas only.

Technical Details

Certificates & Approvals

  • Manufactured under the auspices of an ISO 9001:2008 quality & ISO 14001:2004 environmental management systems.
  • 2004/42/EC EU limit value for this product (cat.A/j sb): 500g/l (2010).

Notes

  • An induction period of 20 minutes after mixing is required if material temperatures are below 10oC*

Technical Info

Components: Two Components
Type: Solvent Based
Finish: Eggshell
Stock Colours: Grey Aluminium
Tintable: No
VOC Content: 373 g/L
Volume Solids: 56% (mixed)
Suitable Substrates: Ideally suited for surfaces and structures on which thorough blast cleaning may not be feasible or practical
Application Method: Brush, Roller, Airless Spray or Conventional Air Spray
Theoretical Coverage: 7.5 m2/L/coat
Wet Film Thickness (WFT): 134 microns/coat
Dry Film Thickness (DFT): 75 microns/coat
Induction Time: -
Pot Life: 8 hours at 20°C*
Surface Dry: 2 hours at 20°C
Overcoatable: After minimum 3 hours at 20°C
Recommended number of coats: 1 coat
Cleaner / Thinner: Bradite Thinner TE36
Shelf Life: 12 months minimum in original unopened containers
Packaging: Available in 4.5 Litres